In-Situ Characterization of Microstructural Changes in Alloy 718 during High-Temperature Low-Cycle Fatigue

Publikation: Beitrag in FachzeitschriftArtikelForschungPeer-Review

Forschungs-netzwerk anzeigen

Details

OriginalspracheEnglisch
Aufsatznummer1871
FachzeitschriftMetals
Jahrgang12
Ausgabenummer11
PublikationsstatusVeröffentlicht - 2 Nov. 2022

Abstract

Components made of nickel-based alloys are typically used for high-temperature applications because of their high corrosion resistance and very good creep and fatigue strength, even at temperatures around 1000 °C. Corrosive damage can significantly reduce the mechanical properties and the expected remaining service life of components. In the present study, a new method was introduced to continuously determine the change in microstructure occurring as a result of exposure to high temperature and cyclic mechanical loading. For this purpose, the conventional low-cycle fatigue test procedure was modified and a non-destructive, electromagnetic testing technique was integrated into a servohydraulic test rig to monitor the microstructural changes. The measured values correlate with the magnetic material properties of the specimen, allowing the microstructural changes in the specimen’s subsurface zone to be analyzed upon high-temperature fatigue. Specifically, it was possible to show how different loading parameters affect the maximum chromium depletion as well as the depth of chromium depletion, which influences the magnetic properties of the nickel-based material. It was also observed that specimen failure is preceded by a certain degree of microstructural change in the subsurface zone. Thus, the integration of the testing technology into a test rig opens up new possibilities for improved prediction of fatigue failure via the continuous recording of the microstructural changes.

ASJC Scopus Sachgebiete

Zitieren

In-Situ Characterization of Microstructural Changes in Alloy 718 during High-Temperature Low-Cycle Fatigue. / Barton, Sebastian; Weiss, Maximilian Karl-Bruno; Maier, Hans Jürgen.
in: Metals, Jahrgang 12, Nr. 11, 1871, 02.11.2022.

Publikation: Beitrag in FachzeitschriftArtikelForschungPeer-Review

Download
@article{97193df106ce48d59f70ae3ff14107f2,
title = "In-Situ Characterization of Microstructural Changes in Alloy 718 during High-Temperature Low-Cycle Fatigue",
abstract = "Components made of nickel-based alloys are typically used for high-temperature applications because of their high corrosion resistance and very good creep and fatigue strength, even at temperatures around 1000 °C. Corrosive damage can significantly reduce the mechanical properties and the expected remaining service life of components. In the present study, a new method was introduced to continuously determine the change in microstructure occurring as a result of exposure to high temperature and cyclic mechanical loading. For this purpose, the conventional low-cycle fatigue test procedure was modified and a non-destructive, electromagnetic testing technique was integrated into a servohydraulic test rig to monitor the microstructural changes. The measured values correlate with the magnetic material properties of the specimen, allowing the microstructural changes in the specimen{\textquoteright}s subsurface zone to be analyzed upon high-temperature fatigue. Specifically, it was possible to show how different loading parameters affect the maximum chromium depletion as well as the depth of chromium depletion, which influences the magnetic properties of the nickel-based material. It was also observed that specimen failure is preceded by a certain degree of microstructural change in the subsurface zone. Thus, the integration of the testing technology into a test rig opens up new possibilities for improved prediction of fatigue failure via the continuous recording of the microstructural changes.",
keywords = "alloy 718, chromium depletion, fatigue, non-destructive testing, oxidation",
author = "Sebastian Barton and Weiss, {Maximilian Karl-Bruno} and Maier, {Hans J{\"u}rgen}",
note = "Funding Information: This research was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) –SFB 871/3 –119193472. Funding Information: The authors thank Deutsche Forschungsgemeinschaft for financial support. The publication of this article was funded by the Open Access Fund of the Leibniz Universit{\"a}t Hannover.",
year = "2022",
month = nov,
day = "2",
doi = "10.3390/met12111871",
language = "English",
volume = "12",
journal = "Metals",
issn = "2075-4701",
publisher = "Multidisciplinary Digital Publishing Institute",
number = "11",

}

Download

TY - JOUR

T1 - In-Situ Characterization of Microstructural Changes in Alloy 718 during High-Temperature Low-Cycle Fatigue

AU - Barton, Sebastian

AU - Weiss, Maximilian Karl-Bruno

AU - Maier, Hans Jürgen

N1 - Funding Information: This research was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) –SFB 871/3 –119193472. Funding Information: The authors thank Deutsche Forschungsgemeinschaft for financial support. The publication of this article was funded by the Open Access Fund of the Leibniz Universität Hannover.

PY - 2022/11/2

Y1 - 2022/11/2

N2 - Components made of nickel-based alloys are typically used for high-temperature applications because of their high corrosion resistance and very good creep and fatigue strength, even at temperatures around 1000 °C. Corrosive damage can significantly reduce the mechanical properties and the expected remaining service life of components. In the present study, a new method was introduced to continuously determine the change in microstructure occurring as a result of exposure to high temperature and cyclic mechanical loading. For this purpose, the conventional low-cycle fatigue test procedure was modified and a non-destructive, electromagnetic testing technique was integrated into a servohydraulic test rig to monitor the microstructural changes. The measured values correlate with the magnetic material properties of the specimen, allowing the microstructural changes in the specimen’s subsurface zone to be analyzed upon high-temperature fatigue. Specifically, it was possible to show how different loading parameters affect the maximum chromium depletion as well as the depth of chromium depletion, which influences the magnetic properties of the nickel-based material. It was also observed that specimen failure is preceded by a certain degree of microstructural change in the subsurface zone. Thus, the integration of the testing technology into a test rig opens up new possibilities for improved prediction of fatigue failure via the continuous recording of the microstructural changes.

AB - Components made of nickel-based alloys are typically used for high-temperature applications because of their high corrosion resistance and very good creep and fatigue strength, even at temperatures around 1000 °C. Corrosive damage can significantly reduce the mechanical properties and the expected remaining service life of components. In the present study, a new method was introduced to continuously determine the change in microstructure occurring as a result of exposure to high temperature and cyclic mechanical loading. For this purpose, the conventional low-cycle fatigue test procedure was modified and a non-destructive, electromagnetic testing technique was integrated into a servohydraulic test rig to monitor the microstructural changes. The measured values correlate with the magnetic material properties of the specimen, allowing the microstructural changes in the specimen’s subsurface zone to be analyzed upon high-temperature fatigue. Specifically, it was possible to show how different loading parameters affect the maximum chromium depletion as well as the depth of chromium depletion, which influences the magnetic properties of the nickel-based material. It was also observed that specimen failure is preceded by a certain degree of microstructural change in the subsurface zone. Thus, the integration of the testing technology into a test rig opens up new possibilities for improved prediction of fatigue failure via the continuous recording of the microstructural changes.

KW - alloy 718

KW - chromium depletion

KW - fatigue

KW - non-destructive testing

KW - oxidation

UR - http://www.scopus.com/inward/record.url?scp=85141671568&partnerID=8YFLogxK

U2 - 10.3390/met12111871

DO - 10.3390/met12111871

M3 - Article

VL - 12

JO - Metals

JF - Metals

SN - 2075-4701

IS - 11

M1 - 1871

ER -

Von denselben Autoren