Details
| Originalsprache | Englisch |
|---|---|
| Titel des Sammelwerks | Proceedings of the 2024 IEEE 5th International Conference on Dielectrics, ICD 2024 |
| Herausgeber (Verlag) | Institute of Electrical and Electronics Engineers Inc. |
| ISBN (elektronisch) | 9798350308976 |
| ISBN (Print) | 979-8-3503-0898-3 |
| Publikationsstatus | Veröffentlicht - 30 Juni 2024 |
| Veranstaltung | 5th IEEE International Conference on Dielectrics, ICD 2024 - Toulouse, Frankreich Dauer: 30 Juni 2024 → 4 Juli 2024 |
Publikationsreihe
| Name | Proceedings of the IEEE International Conference on Dielectrics |
|---|---|
| ISSN (Print) | 2834-8303 |
| ISSN (elektronisch) | 2834-8311 |
Abstract
In this contribution, an investigation about the influence of voltage harmonics on the breakdown voltage of a composite material intended for the use of dry-type transformers produced under the filament winding technology is discussed. A dielectric strength measurement was performed on samples of a composite applying voltage with different waveforms With the intention of recreating the structural disposition of the material, which originates as a result of the manufacturing process by rolling filaments, which are previously impregnated on a resin bath, on a rotating mandrel, a special arrangement has been used for the manufacture of the test objects, consisting of plates with fiberglass bundles under mechanical tension in an epoxy resin matrix. Test samples were exposed to six different voltage waveforms, differing in their total harmonic distortion (THD). The test voltage is generated through a programmable source and a high voltage test transformer. The performed measurements show differences on the RMS value of the breakdown voltage of the material according to the total harmonic distortion. A comparison between the values based on the RMS values and the peak values is given.
ASJC Scopus Sachgebiete
- Ingenieurwesen (insg.)
- Elektrotechnik und Elektronik
- Werkstoffwissenschaften (insg.)
- Elektronische, optische und magnetische Materialien
- Werkstoffwissenschaften (insg.)
- Oberflächen, Beschichtungen und Folien
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
Proceedings of the 2024 IEEE 5th International Conference on Dielectrics, ICD 2024. Institute of Electrical and Electronics Engineers Inc., 2024. (Proceedings of the IEEE International Conference on Dielectrics).
Publikation: Beitrag in Buch/Bericht/Sammelwerk/Konferenzband › Aufsatz in Konferenzband › Forschung › Peer-Review
}
TY - GEN
T1 - Influence of Harmonic Distortion on the Breakdown Voltage of a Composite Material for the Use in Dry Type Transformers
AU - Torres, Javier
AU - Homeier, Kristin
AU - Stahl, Laureen
AU - Werle, Peter
N1 - Publisher Copyright: © 2024 IEEE.
PY - 2024/6/30
Y1 - 2024/6/30
N2 - In this contribution, an investigation about the influence of voltage harmonics on the breakdown voltage of a composite material intended for the use of dry-type transformers produced under the filament winding technology is discussed. A dielectric strength measurement was performed on samples of a composite applying voltage with different waveforms With the intention of recreating the structural disposition of the material, which originates as a result of the manufacturing process by rolling filaments, which are previously impregnated on a resin bath, on a rotating mandrel, a special arrangement has been used for the manufacture of the test objects, consisting of plates with fiberglass bundles under mechanical tension in an epoxy resin matrix. Test samples were exposed to six different voltage waveforms, differing in their total harmonic distortion (THD). The test voltage is generated through a programmable source and a high voltage test transformer. The performed measurements show differences on the RMS value of the breakdown voltage of the material according to the total harmonic distortion. A comparison between the values based on the RMS values and the peak values is given.
AB - In this contribution, an investigation about the influence of voltage harmonics on the breakdown voltage of a composite material intended for the use of dry-type transformers produced under the filament winding technology is discussed. A dielectric strength measurement was performed on samples of a composite applying voltage with different waveforms With the intention of recreating the structural disposition of the material, which originates as a result of the manufacturing process by rolling filaments, which are previously impregnated on a resin bath, on a rotating mandrel, a special arrangement has been used for the manufacture of the test objects, consisting of plates with fiberglass bundles under mechanical tension in an epoxy resin matrix. Test samples were exposed to six different voltage waveforms, differing in their total harmonic distortion (THD). The test voltage is generated through a programmable source and a high voltage test transformer. The performed measurements show differences on the RMS value of the breakdown voltage of the material according to the total harmonic distortion. A comparison between the values based on the RMS values and the peak values is given.
KW - breakdown voltage
KW - harmonic
KW - THD
UR - http://www.scopus.com/inward/record.url?scp=85202292580&partnerID=8YFLogxK
U2 - 10.1109/ICD59037.2024.10613233
DO - 10.1109/ICD59037.2024.10613233
M3 - Conference contribution
AN - SCOPUS:85202292580
SN - 979-8-3503-0898-3
T3 - Proceedings of the IEEE International Conference on Dielectrics
BT - Proceedings of the 2024 IEEE 5th International Conference on Dielectrics, ICD 2024
PB - Institute of Electrical and Electronics Engineers Inc.
T2 - 5th IEEE International Conference on Dielectrics, ICD 2024
Y2 - 30 June 2024 through 4 July 2024
ER -